Phosphonated pbi fiber

ABSTRACT

A fiber is made with a polybenzimidazole (PBI) polymer with a phosphoric acid pick-up (APU) in the range of 1-25% (PBI-p fiber). The PBI-p fiber may have a LOI≥50% and/or an initial thermal decomposition temperature in air of ≥555° C. A method of making a phosphonated polybenzimidazole fiber comprises the steps of: spinning an untreated PBI resin into a PBI fiber; treating the PBI fiber with phosphoric acid, and thereby obtaining a PBI fiber with 1-25 wt. % phosphoric acid APU.

RELATED APPLICATIONS

This application claims the benefit of co-pending U.S. patent application Ser. No. 15/193,206 filed Jun, 27, 2016, now U.S. Patent No. ______, which claimed the benefit of U.S. provisional patent application No. 62/188,812 filed Jul. 6, 2015, both of which are incorporated herein by reference.

FIELD OF THE INVENTION

The instant invention is directed to a polybenzimidazole fiber.

BACKGROUND

In the article, History and Development of Polybenzimidazole by E. J. Powers and G. A. Serad (presented on Apr. 15-18, 1986 and published in High Performance Polymers: Their Origin and Development), it is disclosed that a polybenzimidazole (PBI) polymer with 27 wt. % phosphoric acid (H₃PO₄) absorbed (or pick-up) may have utility as a very thermo-oxidatively stable fiber, pages 19-20 and Table XIII. Powers & Serad teach that the phosphonated PBI is made by soaking PBI films in 2% aqueous phosphoric acid, page 20.

Polybenzimidazole fibers, that have been commercially offered up until this time, are sulfonated. This sulfonated PBI fiber has met with great commercial success in, for example, fire fighter's turnout gear, because it has a LOI (limiting oxygen index, ASTM D2863) of around 41.

In an effort to explore for and open up new applications and uses for PBI and articles made from PBI, the inventors have discovered new and more commercially advantageous phosphonated PBI fibers.

SUMMARY OF THE INVENTION

A fiber is made with a polybenzimidazole (PBI) polymer with a phosphoric acid pick-up (APU) in the range of 1-25% (PBI-p fiber). The PBI-p fiber may have a LOI≥50% and/or an onset thermal degradation temperature ≥555° C. determined by Thermo-Gravimetric Analysis (TGA) in air at a 20° C./min heating rate. A method of making a phosphonated polybenzimidazole fiber comprises the steps of: spinning an untreated PBI resin into a PBI fiber; treating the PBI fiber with phosphoric acid, and thereby obtaining a PBI fiber with 1-25 wt. % phosphoric acid APU.

DESCRIPTION OF THE DRAWING

For the purpose of illustrating the invention, there is shown in the drawing a form that is presently preferred; it being understood, however, that this invention is not limited to the precise arrangements and instrumentalities shown.

FIG. 1 is a TGA graph comparing the initial (or onset) thermal degradation temperatures of various PBI fibers in air at a 20° C./min heating rate.

DESCRIPTION OF THE INVENTION

Polybenzimidazole (PBI) fibers, phosphonated in the range of 1-25 wt. % phosphoric acid (or 1-25 wt % acid pick up (or APU) of phosphoric acid), have thermo-oxidative stability equal to or better than commercially available sulfonated PBI fibers (the range includes all sub-ranges included therein). Thereinafter, phosphonated PBI fiber will be referred to as PBI-p fiber, and sulfonated PBI fiber will be referred to as PBI-s fiber. In another embodiment, the PBI-p fiber has a phosphoric acid APU in the range of 4-20 wt. %. In still another embodiment, the PBI-p fiber has a phosphoric acid APU in the range of 8-24 wt. %. In still another embodiment, the PBI-p has a phosphoric acid pick-up in the range of 12-20 wt. %. In yet another embodiment, the PBI-p fiber has a phosphoric acid APU of about 17 wt. %. In still another embodiment, the PBI-p fiber may have an APU in the range of lower end-upper end, where the lower end of the weight range may be 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, and 11, and the upper end of the weight range may be: 25, 24, 23, 22, 21, 20, 19, 18, 17, 16, 15, 14, 13, 12, 11, and 10.

PBI-p fibers may have any LOI (Limiting Oxygen Index—ASTM D2863). PBI-p fibers may have a LOI of about 47+% (≥47%). PBI-p fibers may have a LOI of 50+% (≥50%). PBI-p fibers may have a LOI of 55+% (≥55%). In one embodiment, PBI-p fibers may have a LOI of 60+% (≥60%). PBI-p fiber may have a LOI of ≥60% at ≥1% or 4% APU phosphoric acid. PBI-p fiber may have a LOI in a range of about 60-75% at ≥1% or 4% APU phosphoric acid. PBI-p fiber may have a LOI of ≥60% at about 4-25% APU phosphoric acid. PBI-p fiber may have a LOI in a range of about 60-75% at 4-25% APU phosphoric acid. PBI-p fiber may have a LOI in a range of about 60-75% at lower end-upper limit % APU phosphoric acid, where the lower end of the weight range may be 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, and 11, and the upper limit is chosen from 25, 24, 23, 22, 21, 20, 19, 18, 17, 16, 15, 14, 13, 12, 11, and 10. PBI-p fiber may have a LOI of about 62.3% at about 7% APU phosphoric acid. PBI-p fiber may have a LOI of about 65.5% at about 12% APU phosphoric acid. PBI-p fiber may have a LOI of about 63.5% at about 17% APU phosphoric acid. Accordingly, one may obtain a thermo-oxidatively stable fiber without a 27 wt. % phosphoric acid pick-up. This is important because of the negative implications associated with phosphates in the environment. The LOI of PBI-s fibers is in the range of 41-44%.

In Thermal Gravimetric Analysis (TGA), changes of sample weight are measured as a function of increasing temperature. A sharp weight loss at high temperature often indicates decomposition of the sample. PBI-p fibers may have any temperature of onset of thermal decomposition in air, as determined by thermo-gravimetric analysis (TGA). TGA tests (using a TA Instrument Model TGA Q500) are conducted for a PBI-s sample and a PBI-p sample in air at a 20° C./min heating rate to up to 1000° C. The results are shown in FIG. 1. In the tests, PBI-s fiber sample has an initial thermal decomposition temperature of 551° C. and PBI-p fiber sample has an initial thermal decomposition temperature of ≥555° C. under the same testing conditions. For TGA tests in air at a 20° C./min heating rate, PBI-p fiber may have an initial thermal decomposition temperature in a range of about 555-625° C. at ≥1 wt. % APU phosphoric acid. PBI-p fiber may have an initial thermal decomposition temperature of ≥565° C. at about 4-25% APU phosphoric acid. PBI-p fiber may have an initial thermal decomposition temperature in a range of about 565-625° C. at 4-25% APU phosphoric acid. PBI-p fiber may have an initial thermal decomposition temperature in a range of about 565-625° C. at lower end-upper limit % APU phosphoric acid, where the lower end of the weight range may be 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, and 11, and the upper limit is chosen from 25, 24, 23, 22, 21, 20, 19, 18, 17, 16, 15, 14, 13, 12, 11, and 10. The following is actual test data: PBI-p fiber has an initial thermal decomposition temperature of about 567° C. at about 7% APU phosphoric acid; PBI-p fiber has an initial thermal decomposition temperature of about 577° C. at about 12% APU phosphoric acid; and PBI-p fiber has an initial thermal decomposition temperature of about 592° C. at about 17% APU phosphoric acid.

PBI-p fiber may have any denier. PBI-p fiber may have a denier no greater than 6 denier per filament (dpf). PBI-p fiber may have a denier in the range of 0.1-5 dpf. In one embodiment, the fiber denier is in the range of 1-3 dpf.

Polybenzimidazoles (PBI) resins are a known class of compounds. See, for example, US Re26065; U.S. Pat. Nos. 3,433,772; 4,717,764; and 7,696,302, each of which is incorporated herein by reference. Polybenzimidazole (PBI) resin may be any known PBI resin. PBI resins also refers to blends of PBI resins with other polymers, co-polymers of PBI, and combinations thereof. The PBI resin component may be the entire (100%) resin component or a major (i.e., at least 50 wt %) component. In general, PBI resins may be the product of the melt polymerization of a tetraamine (e.g., aromatic and heteroaromatic tetra-amino compounds) and a second monomer being selected from the group consisting of free dicarboxylic acids, alkyl and/or aromatic esters of dicarboxylic acids, alkyl and/or aromatic esters of aromatic or heterocyclic dicarboxylic acid, and/or alkyl and/or aromatic anhydrides of aromatic or heterocyclic dicarboxylic acid. Further details about PBI polymerization may be obtained from U.S. Pat. Nos. Re 26065; 4,506,068; 4,814,530; and US Publication Nos. 2007/0151926 and 2014/0357831 (organic aldehyde adduct route), each of which is incorporated herein by reference. PBI resins and fibers are commercially available from PBI Performance Products, Inc. of Charlotte, N.C.

Examples of PBI polymers include, but are not limited to: poly-2,2′-(m-phenylene) -5, 5′-bibenzimidazole; poly-2,2′-(biphenylene-2″2′″)-5,5′-bibenzimidazole; poly-2,2′-(biphenylene-4″4′″)-5,5′-bibenzimidazole; poly-2,2′-(1″,1″,3″trimethylindanylene)-3″5″-p-phenylene-5,5′-bibenzimidazole; 2,2′-(m-phenylene)-5,5′-bibenzimidazole/2,2-(1″,1″,3″-trimethylindanylene)- 5″,3″-(p-phenylene)-5,5′-bibenzimidazole copolymer; 2,2′-(m-phenylene)-5,5-bibenzimidazole-2,2′-biphenylene-2″,2′″-5,5′-bibenzimidazole copolymer; poly-2,2′-(furylene-2″,5″)-5,5′-bibenzimidazole; poly-2,2′-(naphthalene-1″,6″)-5,5′-bibenzimidazole; poly-2,2′-(naphthalene-2″,6″)-5,5′-bibenzimidazole; poly-2,2′-amylene-5,5′-bibenzimidazole; poly-2,2′-octamethylene-5,5′-bibenzimidazole; poly-2,2′-(m-phenylene)-diimidazobenzene; poly-2,2′-cyclohexenyl-5,5′-bibenzimidazole; poly-2,2′-(m-phenylene)-5,5′-di(benzimidazole)ether; poly-2,2′-(m-phenylene)-5,5′-di(benzimidazole)sulfide; poly-2,2′-(m-phenylene)-5,5′-di(benzimidazole)sulfone; poly-2,2′-(m-phenylene)-5,5′-di(benzimidazole)methane; poly-2,2″-(m-phenylene)-5,5″-di(benzimidazole)propane-2,2; and poly-ethylene-1,2-2,2″-(m-phenylene)-5,5″-dibenzimidazole)ethylene-1,2 where the double bonds of the ethylene groups are intact in the final polymer. Poly-2,2′-(m-phenylene)-5, 5′-bibenzimidazole is preferred.

In general, PBI-p fiber may be made by: spinning PBI resin (without any acid treatment, i.e., untreated), and treating the fibers with phosphoric acid.

Spinning may be by any conventional spinning technique. One such technique is solution spinning where a dope (PBI dissolved in a suitable solvent) is spun through a spinneret, and subsequently taken-up after solvent removal.

Treating may include the steps of applying the phosphoric acid to the untreated fiber, and, after a suitable residence time, removal and/or drying of the treated fiber. Applying the phosphoric acid may be conducted by any conventional method. Conventional methods include, but are not limited to, dipping (e.g., via a bath), spraying, brushing, roller coating, and the like. In one embodiment, the treating may be conducted in a bath of phosphoric acid. In one embodiment, the residence time (time that fiber is immersed in the acid bath) may be in the range of 15-360 seconds. In another embodiment, the residence time may be in the range of 20-180 seconds. In yet another embodiment, the residence time may be in the range of 20-70 seconds. The bath may be at any temperature. In one embodiment, the bath has a temperature in the range of 15-60° C. In another embodiment, the bath has a temperature in the range of 20-50° C. In yet another embodiment, the temperature may be range of 25-40° C. In yet another embodiment, the temperature may be in the range of 30-40° C. The phosphoric acid used in the treatment step may be any concentration of phosphoric acid. In one embodiment, the phosphoric acid (aqueous) has a concentration in the range of 10-85 wt. %. In another embodiment, the phosphoric acid (aqueous) has a concentration in the range of 20-60 wt. %. In still another embodiment, the phosphoric acid (aqueous) has a concentration in the range of 40-60 wt. %. In yet another embodiment, the phosphoric acid (aqueous) has a concentration of about 50 wt. %. While applying the phosphoric acid, the fiber may under tension. In one embodiment, the tension may range from 1.0-25.0 dN (as measured by a conventional tensiometer on a subtow). In another embodiment the tension may be in the range of 2-12 dN. In still another embodiment, the tension may be in the range of 2-8 dN. In yet another embodiment, the tension may be in the range of 2.5-7.5 dN. Removal of excess acid and/or drying may be conducted in any manner. Removal and/or drying may include an optional rinse to remove residual acid.

PBI-p fibers may be used in any application. Such applications include, but are not limited to: textile applications, mechanical applications, and additives for plastics. In the textile applications, the fibers (either staple of filament) may be combined with other fiber to spin yarns. The yarns may be woven or knitted into fabrics. The fabrics may be cut and sewn into garments. These textile processes are conventional. The PBI-p fibers may also be converted to non-wovens by any conventional technique. The mechanical applications include, for example, gaskets and seals.

EXAMPLES

Extruded polybenzimidazole fiber was washed in hot water to remove spinning solvent and then space drawn in a heated oven to improve its tensile properties. The fiber was then treated with 50% (wt) aqueous phosphoric acid by submerging the fibers in a bath for 48-52 seconds from entry to exit of the unit (the fiber was immersed in the liquid for about 25 seconds). The bath temperature was held at 35° C. The fiber was then squeezed to dry it and washed with water at room temperature. The washed fiber was then dried in an air non-contact oven operating at 350° C. The dry fiber was then heat treated in a nitrogen blanketed oven operating at 565° C. to fix the acid within the polymer structure. Subsequent textile treatment processes resulted in the phosphonated fiber being produced as a two inch cut staple fiber. The 1.5 denier per filament (dpf) cut staple fiber had a tenacity of 2.00 g/dN, an elongation at break of 10.88%, and an acid pick-up* of 17-20 wt %. *Acid pick-up values were determined by mass balance, and verified by elemental analysis. Mass balance—Acid Content was derived using a mass balance evaluating the weight gain of the fiber. The moisture is removed from the sample and the remaining mass is divided by the dry PBI from the creel. The balance is then checked with a second balance around the acid concentrations in the bath, waste-water, and consumption. Elemental analysis—Acid Content was derived using elemental analysis by Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES). The ICP-OES method determines the percent of a particular element present in a sample. In the case of the example fiber, ICP-OES determined the presence of 5.51% Phosphorous. However, phosphorous is present on the example fiber as Phosphate (PO₄). Phosphorous is present in Phosphate at approximately 32%. Therefore, the presence of 5.51% Phosphorous tells us that Phosphate (acid) pick-up is approximately 17%.

Preliminary laboratory phosphoric acid treatment of extruded PBI fiber is further illustrated with the data presented in Table below.

Time Time Wt Time Time in in after Drying Acid Estimated Orig. % in in oven oven 2nd Condition Pickup Dry Wt Fiber wt. acid Temp acid H2O 1st drying 2nd drying drying (in oven) (APU) g g used C. Sec Sec Sec Sec g C. wt % Note 1 0.60 0.7 30% room 60 15 300 100 0.68 180  14.3% 2 0.63 0.74 50% room 60 15 300 100 0.76 180  20.8% 3 0.60 0.71 85% room 60 15 300 100 0.67 180  11.0% 4 0.70 0.82 30% room 60 15 300 100 0.78 180  11.9% 5 0.65 0.77 50% room 60 15 300 100 0.79 180  20.7% 6 0.70 0.82 85% room 60 15 300 100 0.83 180  19.1% 7 0.71 0.83 30% room 60 0 300 100 1.14 180  61.6% 8 0.62 0.73 50% room 60 0 300 100 1.29 180 107.9% 9 0.67 0.79 85% room 60 0 300 100 1.88 180 180.0% 10 0.76 0.89 30% 50 60 15 300 100 1 180  32.2% 11 0.65 0.76 50% 50 60 15 300 100 1.02 180  57.9% 12 0.71 0.84 30% 40 60 15 300 100 0.84 180  17.6% 13 0.70 0.82 50% 40 60 15 300 100 1 180  43.5% 14 0.34 0.4 50% 60 60 15 900 100 0.52 105  52.9% with tension 15 0.34 0.4 50% 60 60 15 900 100 0.51 105  50.0% 16 0.36 0.42 50% 45 60 15 1800 0 0.51 105  42.9% 17 0.34 0.4 50% 45 60 15 1800 0 0.53 105  55.9% 18 0.38 0.45 50% 45 60 15 1800 0 0.48 105  25.5% with tension 19 0.37 0.44 50% 45 60 15 1800 0 0.46 105  23.0% with tension

The present invention may be embodied in other forms without departing from the spirit and the essential attributes thereof, and, accordingly, reference should be made to the appended claims, rather than to the foregoing specification, as indicated the scope of the invention. 

We claim:
 1. A fiber comprises a polybenzimidazole (PBI) polymer with a phosphoric acid pick-up (APU) in the range of 1-25%.
 2. The fiber of claim 1 wherein the LOI (Limiting Oxygen Index) is about ≥47%.
 3. The fiber of claim 1 wherein the initial thermal decomposition temperature in air is about ≥555° C.
 4. The fiber of claim 1 having a denier no greater than 6 dpf.
 5. The fiber of claim 1 is a staple or a filament.
 6. A yarn comprises the fiber of claim
 1. 7. A fabric comprises the yarn of claim
 6. 8. The fabric of claim 7 is a woven fabric or a knitted fabric.
 9. A garment comprises the fabric of claim
 7. 10. A nonwoven comprises the fiber of claim
 1. 11. A fiber comprises a polybenzimidazole (PBI) polymer with a phosphoric acid pick-up (APU) in the range of 1-25%, and having at least one of the following: a LOI (Limiting Oxygen Index) of about ≥47%, and an initial thermal decomposition temperature in air of about ≥555° C.
 12. The fiber of claim 11 having a denier no greater than 6 dpf.
 13. The fiber of claim 11 is a staple or a filament.
 14. A yarn comprises the fiber of claim
 11. 15. A fabric comprises the yarn of claim
 14. 16. The fabric of claim 15 is a woven fabric or a knitted fabric.
 17. A garment comprises the fabric of claim
 15. 18. A nonwoven comprises the fiber of claim
 11. 19. A fabric comprises a yarn including a fiber including a polybenzimidazole (PBI) polymer with a phosphoric acid pick-up (APU) in the range of 1-25%. 